- Using zinc to protect steel from corrosion (hot-dip galvanizing) is a 150-year-old practice!
- Corrosion is caused by the inherent tendency of metals, when subjected to air and moisture, to revert to their original earthly forms, usually an ore state. They do this through a chemical or electrochemical reaction with the environment.
- Galvanizer’s kettles are set at temperatures ranging between 815 F and 850 F (435 C to 454 C).
- A galvanizer knows a piece of steel should be immersed for a specific amount of time in order for the metallurgical reaction between zinc and iron to reach completion. The completion of the metallurgical reaction is observed when bubbling of the molten zinc in the kettle stops. At this point, the galvanizing is complete and the steel is removed from the kettle to cool.
- Galvanizers can hot-dip galvanize a piece of steel that is larger than the kettle dimensions; it’s called progressive dipping.
- Zinc seals the underlying steel from contact with its environment. If the steel is exposed to the elements due to mechanical damage, the surrounding zinc corrodes sacrificially, protection the underlying steel from corrosive attack.
- The zinc coating on galvanized steel is uniform: inside, outside, corners and edges.
- The hot-dip galvanized reinforcing steel bond with concrete is at least as great as the bond of bare steel to concrete.
- When the Brooklyn Bridge was built, over 14,500 miles of hot-dip galvanized wire were used for its four main cables. Over 100 years later when the bridge underwent massive rehabilitation, the hot-dip galvanized wire was in excellent condition. Hot-dip galvanized steel lasts longer today than it did 20 years ago. Because of environmental laws, our air is cleaner and less contaminated with corrosive emissions.
- A reddish-brown staining infrequently develops on the surface of a newly galvanized piece of steel that is comprised entirely of intermetallic layers. The steel is not rusting; there is just a very small amount of iron in the zinc-iron alloy layers that is oxidizing, causing the staining to occur. This does not cause any adverse effects on the corrosion performance of the galvanized steel.
- Corrosion annually costs the US economy 3.2 percent of the gross national product, over $423 billion. Indirect costs to the public could raise the percentage as much as 5-11 percent. Some indirect costs of corrosion are: lost productivity due to traffic delays, accidents caused by corroded hand and guardrails, excessive use of nature’s raw materials and energy to replace corroded steel.
- Based on a study by NACE International (The Corrosion
Society), members of Congress, and the Department of Transportation (DOT),
better corrosion management can be achieved using preventive strategies at
every level of involvement (owner, operator, user, government, Federal
regulators, and general public).
Leopad Group a leading provider of corrosion
protection services ranges from the scope of blasting and painting, insulation,
thermal spray application, passive fire protection, refractory and other
services such as scaffolding, cable tray systems and cathode protection.
We are a
Malaysian company with close to 3000 staff and over 10 offices and fabrication
yards throughout the country. Leopad Group is dedicated to being the market
leader for corrosion protection and provide the highest standards in the
industry with the convenience of providing multi-disciplinary services through
a single point of contact.
For further
enquiries on our services, please contact our Business Development Department
at +603-22600200 , website www.leopad.com or email at hq@leopad.com
No comments:
Post a Comment